The difference between 6060 aluminum plate and 6063 aluminum plate
-
crushermachine2
- Posts: 35
- Joined: May 25th, 2018, 4:16 am
Differences in their material composition:
The chemical composition and processing properties of 6060 aluminum sheet and 6063 aluminum sheet are similar, but not identical.
Material composition of 6060 aluminum plate: Si: 0.3-0.6; Iron: 0.1-0.3; Cu: 0.1; Mn: 0.1; mg: 0.35-0.6; Chromium: – Zinc: 0.1; ; ale: quantity.
Material composition of 6063 aluminum plate: aluminum al: balance; si: 0.20-0.6; Cu: ≤0.10; mg: 0.45-0.9; Zn: ≤0.10; Mn: ≤0.10; ti: ≤0.10; Cr: ≤0.10; Fe : 0.000 ~ 0.350; Note: Single: ≤ 0.05; Total: ≤ 0.15;
Features of 6060 aluminum plate:
Tensile strength σb (MPa): ≥ 470
Conditional yield strength σ0.2 (MPa): ≥420
Elongation δ5 (%): ≥ 6
Features: 1. High strength heat treatable alloy. 2. Good mechanical properties. 3. Good usability. 4. Easy to process and good wear resistance. 5. Good corrosion resistance and good oxidation resistance
Features of 6063 aluminum plate:
6063 aluminum plate belongs to aluminum magnesium silicon alloy and is widely used. Especially in the construction industry, it is the most promising alloy. Good corrosion resistance, excellent weldability, good cold workability and moderate strength. Luhua Aluminum's 6063 aluminum plate manufacturers are of high quality and low price.
6063 aluminum sheet is a low-alloy aluminum-magnesium-silicon high plasticity alloy with many properties:
1. Heat treatment strengthening, high impact toughness.
2. It has excellent thermoplasticity and can be extruded into complex structures at high speed. such as thin walls. It also has a wide quenching temperature range and low quenching sensitivity, as long as the temperature is higher than the quenching temperature after extrusion and forging demoulding. Can be water sprayed or water quenched.
The chemical composition and processing properties of 6060 aluminum sheet and 6063 aluminum sheet are similar, but not identical.
Material composition of 6060 aluminum plate: Si: 0.3-0.6; Iron: 0.1-0.3; Cu: 0.1; Mn: 0.1; mg: 0.35-0.6; Chromium: – Zinc: 0.1; ; ale: quantity.
Material composition of 6063 aluminum plate: aluminum al: balance; si: 0.20-0.6; Cu: ≤0.10; mg: 0.45-0.9; Zn: ≤0.10; Mn: ≤0.10; ti: ≤0.10; Cr: ≤0.10; Fe : 0.000 ~ 0.350; Note: Single: ≤ 0.05; Total: ≤ 0.15;
Features of 6060 aluminum plate:
Tensile strength σb (MPa): ≥ 470
Conditional yield strength σ0.2 (MPa): ≥420
Elongation δ5 (%): ≥ 6
Features: 1. High strength heat treatable alloy. 2. Good mechanical properties. 3. Good usability. 4. Easy to process and good wear resistance. 5. Good corrosion resistance and good oxidation resistance
Features of 6063 aluminum plate:
6063 aluminum plate belongs to aluminum magnesium silicon alloy and is widely used. Especially in the construction industry, it is the most promising alloy. Good corrosion resistance, excellent weldability, good cold workability and moderate strength. Luhua Aluminum's 6063 aluminum plate manufacturers are of high quality and low price.
6063 aluminum sheet is a low-alloy aluminum-magnesium-silicon high plasticity alloy with many properties:
1. Heat treatment strengthening, high impact toughness.
2. It has excellent thermoplasticity and can be extruded into complex structures at high speed. such as thin walls. It also has a wide quenching temperature range and low quenching sensitivity, as long as the temperature is higher than the quenching temperature after extrusion and forging demoulding. Can be water sprayed or water quenched.